SabikGeloyXTWM206resin adalahGenerasi berikutnya Geloy XTW ASA untuk aplikasi eksterior panas tinggi. ketahanan cuaca dan ketahanan yang luar biasa.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 46 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 37 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 43 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 36 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 2.7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 26 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 27 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2360 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 74 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2450 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 36 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 2.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 36 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2350 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 64 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2380 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 210 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 36 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 11 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 97 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 84 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.4E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pass85 | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 95 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 99 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 98 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 84 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.09 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.75 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 8.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.09 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 9 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/05/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 85 - 90 | °C |
| Waktu Pengeringan | 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 240 - 270 | °C |
| Suhu Nozzle | 220 - 255 | °C |
| Suhu depan - Zona 3 | 230 - 260 | °C |
| Tengah - Zona 2 Suhu | 220 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 215 - 250 | °C |
| Suhu Cetakan | 60 - 85 | °C |
| Tekanan Belakang | 0.3 - 1 | MPa |
| Kecepatan sekrup | 30 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:04/05/2004 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Geloy XTWM206.pdf |
|