SabikGeloyXP4025Eresin adalahcampuran ASA/PC yang dimodifikasi panas tinggi, untuk aplikasi eksterior otomotif.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 145 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 5 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 15 | % | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 15 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2350 | MPa | ISO 178 |
| Kekerasan, H358/30 | 98 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 115 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -10°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 -40°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 14 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.25 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 60°C, aliran | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Uji tekanan bola, perkiraan maksimum | 90 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 104 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 107 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 104 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 86 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.7 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/10,0 kg | 5 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 18 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+16 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 27 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 4.3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.18 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.021 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 225 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 225 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 20 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:01/20/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.05 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 230 - 260 | °C |
| Suhu depan - Zona 3 | 240 - 270 | °C |
| Tengah - Zona 2 Suhu | 230 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 220 - 250 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 50 - 70 | °C |
| Sumber GMD, terakhir diperbarui:01/20/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
Silakan hubungi kami untuk penawaran spesifik dan rincian lebih lanjut.
| Merek | Seri | Model |
| Sabik | Geloy | HRA222F-10000 |
| HRA222F-7T2D242 | ||
| XP4034-BK1041 | ||
| XP4034-NA1000 | ||
| XTPMFR10-WH9F029 |
.
Dalam beberapa tahun terakhir, kami telah mengembangkan pasar domestik dan secara aktif mengeksplorasi pasar luar negeri.Hingga saat ini, kami telah menyediakan produk dan layanan berkualitas tinggi untuk lebih dari 1.000 pelanggan di berbagai industri, termasuk: elektronik dan peralatan listrik, medis, makanan,elektronik otomotif, komunikasi optoelektronik, energi fotovoltaik baru, pengolahan air, transportasi dan industri lainnya.
Samtion Chemical memasok plastik teknik dan bahan khusus yang dimodifikasi dari S-Plastics dan merek lain. Produk asli kami dijamin,dengan kualifikasi lengkap dan kapasitas pasokan yang unggul dan keuntungan harga.
Setiap batch produk kami adalah subjek inspeksi kualitas yang ketat untuk memastikan pasokan asli. Semua produk memiliki sertifikat MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA!!
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
|
S-Plastics Geloy XP4025E.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|