SabikGeloyXTWM200resin adalahASA resin untuk cetakan injeksi aliran yang sangat baik, panas rendah, warna dan kemampuan cuaca luar ruangan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 2.8 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 20 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2390 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2570 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 34 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 2.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 28 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2700 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 72 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2450 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 65 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 24 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 40 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 95 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 77 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | NA | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 88 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 93 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.1 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.4 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 15 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.1 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.55 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.25 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/10,0 kg | 12 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:05/27/2004 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 235 - 265 | °C |
| Suhu Nozzle | 215 - 250 | °C |
| Suhu depan - Zona 3 | 225 - 255 | °C |
| Tengah - Zona 2 Suhu | 215 - 250 | °C |
| Bagian belakang - Zona 1 Suhu | 210 - 245 | °C |
| Suhu Cetakan | 60 - 85 | °C |
| Tekanan Belakang | 0.3 - 1 | MPa |
| Kecepatan sekrup | 30 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:05/27/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Geloy XTWM200.pdf |
|