SabikGeloyXTWE480resin adalahAnti goresan Geloy dengan ketahanan cuaca yang sangat baik, aliran tinggi, dan kualitas permukaan yang baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 36 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 21 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2470 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 70 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2060 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 38 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 25 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 70 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2410 | MPa | ISO 178 |
| Tes Kekerasan Pensil, 1kgf | F | - | ASTM D 3363 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 49 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 27 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 6 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 3 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 78 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 73 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 8.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 79 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 73 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.15 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 38 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.15 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:07/28/2008 | |||
| Parameter | ||
| Ekstrusi Profil | Nilai | Satuan |
| Suhu Pengeringan | 75 - 85 | °C |
| Waktu Pengeringan | 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 200 - 230 | °C |
| Barel - Zona 1 Suhu | 205 - 220 | °C |
| Barel - Zona 2 Suhu | 210 - 225 | °C |
| Barel - Zona 3 Suhu | 215 - 225 | °C |
| Barel - Zona 4 Suhu | 215 - 225 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu adaptor | 200 - 225 | °C |
| Suhu mati | 210 - 225 | °C |
| Suhu Kalibrator | 50 - 70 | °C |
| Sumber GMD, terakhir diperbarui:07/28/2008 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Geloy XTWE480.pdf |
|