SabikGeloyXTWE291resin adalahCycoloy kompatibel, cuaca yang sangat baik. coextrusion capstock kelas asa. Thermoformable. spa dan kendaraan luar.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 36 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 15 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3000 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2650 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 53 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 35 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 2.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 52 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 74 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2600 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 95 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 30 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 2 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 89 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 76 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 88 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 90 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 78 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.1 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.35 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 0.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.13 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.8 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 2 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:12/06/2005 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan | 220 - 245 | °C |
| Barel - Zona 1 Suhu | 180 - 225 | °C |
| Barel - Zona 2 Suhu | 190 - 230 | °C |
| Barel - Zona 3 Suhu | 205 - 240 | °C |
| Barel - Zona 4 Suhu | 210 - 245 | °C |
| Suhu adaptor | 210 - 245 | °C |
| Suhu mati | 210 - 245 | °C |
| Temperature Roll Stack - Atas | 70 - 100 | °C |
| Temperature Roll Stack - Pertengahan | 70 - 95 | °C |
| Roll Stack Temp - Bagian bawah | 65 - 90 | °C |
| Sumber GMD, terakhir diperbarui:12/06/2005 | ||
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Geloy XTWE291.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|