SabikGeloyXP2003resin adalahPaduan ASA + PVC. ketahanan cuaca yang sangat baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 38 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 30 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 48 | MPa | ASTM D 790 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 51 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1930 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 1580 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 102 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 961 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 106 | J/m | ASTM D 256 |
| Gardner, 23°C | 33 | J | ASTM D 3029 |
| Gardner, -30°C | 10 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 56 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 28 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 82 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 73 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 8.46E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.21 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 4.5 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Berkilau, tidak bertekstur, 60 derajat | 90 | - | ASTM D 523 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 7.2E+14 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.2E+15 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 18.6 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 32 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 3.54 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.0031 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 3 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| UL diakui, 94V-1 Flame Class Rating (3) | 3.3 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 3.3 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 65 - 70 | °C |
| Waktu Pengeringan | 2 - 3 | jam |
| Waktu pengeringan (kumulatif) | 3 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 195 - 210 | °C |
| Suhu Nozzle | 190 - 205 | °C |
| Suhu depan - Zona 3 | 180 - 195 | °C |
| Tengah - Zona 2 Suhu | 170 - 190 | °C |
| Bagian belakang - Zona 1 Suhu | 165 - 175 | °C |
| Suhu Cetakan | 25 - 60 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 30 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Geloy XP2003.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|