SabikGeloyHRE250resin adalahPengaruh tinggi, tahan cuaca, tahan api, pemuatan injeksi kelas Polikarbonat / paduan AES.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 120 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2200 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 699 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 100 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.17 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 31 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:06/18/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 100 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Suhu Peleburan | 260 - 280 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:06/18/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |