SabikGeloyHRA222resin adalahpaduan tahan api ASA+PC bebas klorin dan bromin untuk proses pencetakan injeksi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 63 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 59 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 66 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | > 100 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | > 100 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2590 | MPa | ASTM D 638 |
| Tekanan tarik, hasil, 5 mm/menit | 62 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 51 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 60 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4.3 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | > 50 | % | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | > 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2520 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 93 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2510 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 385 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, 0°C | 290 | J/m | ASTM D 256 |
| Izod Impact, bernotas 80*10*4 +23°C | 17 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 0°C | 12 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 9 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| CTE, -30°C sampai 80°C, aliran | 6.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C sampai 80°C, xflow | 7.1E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 111 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 102 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 104 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 99 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 88 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Kepadatan | 1.17 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.6 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 260°C/2,16 kg | 13 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL Compliant, 94-5VB Rating (3) | 2.3 | mm | UL 94 oleh GE |
| UL diakui, 94V-2 Flame Class Rating (3) | 0.8 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 2 | mm | UL 94 |
| UL diakui, 94-5VB rating (3) | 2.3 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 29 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:02/01/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 230 - 270 | °C |
| Suhu Nozzle | 220 - 260 | °C |
| Suhu depan - Zona 3 | 230 - 270 | °C |
| Tengah - Zona 2 Suhu | 220 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 200 - 230 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 50 - 70 | °C |
| Sumber GMD, terakhir diperbarui:02/01/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |