SabikGeloyGY2030resin adalahASA bubuk untuk aplikasi tahan cuaca dan dan pencampuran dengan PVC
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 37 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 29 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1790 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 52 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1780 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 35 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 28 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 2.8 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 60.5 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1840 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 52 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1780 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 10 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 8 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 29 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 38 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 11 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 39 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 85 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 77 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 85 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 88 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 79 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.06 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 8.6 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.06 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 220°C/10,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:12/21/2005 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 00.02 - 0.3 | % |
| Suhu Peleburan | 205 - 215 | °C |
| Barel - Zona 1 Suhu | 175 - 205 | °C |
| Barel - Zona 2 Suhu | 175 - 205 | °C |
| Barel - Zona 3 Suhu | 175 - 205 | °C |
| Barel - Zona 4 Suhu | 175 - 205 | °C |
| Suhu adaptor | 150 - 205 | °C |
| Suhu mati | 150 - 205 | °C |
| Sumber GMD, terakhir diperbarui:12/21/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan download lembar data |
|
 |
S-Plastics Geloy GY2030.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|