SabikXenoyXL1339Uresin adalahData yang dihasilkan di laboratorium BOZ. suhu tinggi untuk aplikasi non-kimia tahan diperlukan. UV-stabil.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 49 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2090 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 94 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2090 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 16 | mg/1000cy | ASTM D 1044 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 70 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 699 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, 0°C | 672 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -20°C | 598 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 245 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 224 | J/m | ASTM D 256 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -10°C | 38 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 35 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 -40°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 35 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| CTE, -30°C sampai 30°C, aliran | 7.56E-05 | 1/°C | ASTM D 696 |
| CTE, -30°C sampai 30°C, xflow | 7.92E-05 | 1/°C | ASTM D 696 |
| Konduktivitas Termal | 0.18 | W/m-°C | ASTM C 177 |
| Vicat Softening Temperature, Tingkat A/50 | 140 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 130 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 135 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 125 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.1 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.7 | % | ASTM D 570 |
| Absorpsi air, 50% RH, keseimbangan | 0.2 | % | ASTM D 570 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.5 - 0.8 | % | Metode S-Plastics |
| Rasio Poisson | 0.4 | - | ASTM D 638 |
| Tingkat Volume Peleburan, MVR pada 265°C/1,2 kg | 4 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+14 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.3 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.1 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |