SabikXenoyXD1525resin adalahcampuran PC+PET panas tinggi, dampak dimodifikasi dengan modulus yang meningkat.
aplikasi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 58 | MPa | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 85 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2200 | MPa | ISO 178 |
| Kekerasan, H358/30 | 95 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, bernotas 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 0°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 20 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 15 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.18 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 9.2E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 145 | °C | ISO 306 |
| Ciri-ciri khas (2) | ISO 306 | ||
| Mekanis | Nilai | Satuan | ISO 306 |
| Taber Abrasion, CS-17, 2 kg | 20 | mg/1001cy | ISO 75/Be |
| Tekanan tarik, hasil, 51 mm/menit | 55 | MPa | ISO 75/Ae |
| Tekanan tarik, pecah, 51 mm/menit | 58 | MPa | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.8 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.5 - 0.8 | % | Metode S-Plastics |
| Kepadatan | 1.21 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.7 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/1,2 kg | 6 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+14 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3.3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 3.1 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | IEC 60250 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94HB (3) ((4) | 1.5 | mm | UL 94 oleh GE |
| Sumber GMD, terakhir diperbarui:12/14/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu Nozzle | 260 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 270 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Sumber GMD, terakhir diperbarui:12/14/1999 | ||
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Xenoy XD1525.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|