SabikGeloyEXGY0022resin adalahVFx Ekstrusi untuk Lembar Tiga Lapisan
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 38 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 14 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 50 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 76 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2750 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 53 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 48 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 29.2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2750 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 76 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2780 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 66 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 33 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 4 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 2 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 75 | °C | ASTM D 648 |
| Vicat Softening Temperature, Tingkat B/50 | 86 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 89 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 77 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.14 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 0.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 6.24 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 3 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:07/23/2004 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan | 220 - 245 | °C |
| Barel - Zona 1 Suhu | 180 - 225 | °C |
| Barel - Zona 2 Suhu | 190 - 230 | °C |
| Barel - Zona 3 Suhu | 205 - 240 | °C |
| Barel - Zona 4 Suhu | 210 - 245 | °C |
| Suhu adaptor | 210 - 245 | °C |
| Suhu mati | 210 - 245 | °C |
| Temperature Roll Stack - Atas | 70 - 100 | °C |
| Temperature Roll Stack - Pertengahan | 70 - 95 | °C |
| Roll Stack Temp - Bagian bawah | 65 - 90 | °C |
| Sumber GMD, terakhir diperbarui:07/23/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |