SabikGeloyEXGY007resin adalahKelas ekstrusi gloss terendah adalah GELOY XTW. Akan dipasarkan sebagai XTWE230
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 28 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 32 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 2.5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 80 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1790 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 55 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1880 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 36 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 30 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 25 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1800 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 50 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 2 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 20 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 16 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 85 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 75 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.03E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.12E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 86 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 89 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 77 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.12 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 3 - 5 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 3 - 5 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 3 - 5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.12 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 4 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:02/15/2004 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 00.02 - 0.3 | % |
| Suhu Peleburan | 205 - 215 | °C |
| Barel - Zona 1 Suhu | 175 - 205 | °C |
| Barel - Zona 2 Suhu | 175 - 205 | °C |
| Barel - Zona 3 Suhu | 175 - 205 | °C |
| Barel - Zona 4 Suhu | 175 - 205 | °C |
| Suhu adaptor | 150 - 205 | °C |
| Suhu mati | 150 - 205 | °C |
| Sumber GMD, terakhir diperbarui:02/15/2004 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Geloy EXGY007.pdf |
|