SabikXenoyX6800BMresin adalahBlow mold, dampak dimodifikasi Xenoy
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 48 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 11 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 238 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1690 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 51 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1650 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 31 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 38 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 14.4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 167 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1700 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 48 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1420 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 802 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 186 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 95 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 22 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 129 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 115 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 47 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.7E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.3E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.7E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 118 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 115 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 46 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 2.85 - 3.35 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 4 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.1 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.01 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 9 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:04/27/2007 | |||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 100 - 105 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.01 - 0.03 | % |
| Suhu Peleburan (Parison) | 255 - 265 | °C |
| Barel - Zona 1 Suhu | 250 - 260 | °C |
| Barel - Zona 2 Suhu | 250 - 260 | °C |
| Barel - Zona 3 Suhu | 255 - 260 | °C |
| Barel - Zona 4 Suhu | 255 - 265 | °C |
| Adaptor - Zona 5 Suhu | 255 - 265 | °C |
| Kepala - Zona 6 - Suhu puncak | 255 - 265 | °C |
| Kepala - Zona 7 - Suhu rata-rata | 255 - 265 | °C |
| Kepala - Zona 7 - Suhu bawah | 255 - 265 | °C |
| Kecepatan sekrup | 15 - 50 | rpm |
| Suhu zona pakan ekstruder | 255 - 265 | °C |
| Suhu akumulator | 255 - 265 | °C |
| Suhu Cetakan | 50 - 95 | °C |
| Suhu mati | 255 - 265 | °C |
| Sumber GMD, terakhir diperbarui:04/27/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X6800BM.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|