SabikGeloyCR9020resin adalahASA berkilau tinggi. Bahan tutup tahan cuaca untuk koekstrusi. Termoformasi: Panel bodi untuk traktor, kendaraan rekreasi, dll.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 39 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 15 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 3030 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2750 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 55 | MPa | ISO 527 |
| Modulus tarik, 1 mm/menit | 2800 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 78 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 106 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 32 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 9 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 104 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 94 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 83 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 93 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 82 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.54E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.08E-04 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 99 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 83 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.08 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 7.5 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 220°C/10,0 kg | 8 | g/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:11/27/2001 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan | 220 - 245 | °C |
| Barel - Zona 1 Suhu | 180 - 225 | °C |
| Barel - Zona 2 Suhu | 190 - 230 | °C |
| Barel - Zona 3 Suhu | 205 - 240 | °C |
| Barel - Zona 4 Suhu | 210 - 245 | °C |
| Suhu adaptor | 210 - 245 | °C |
| Suhu mati | 210 - 245 | °C |
| Temperature Roll Stack - Atas | 70 - 100 | °C |
| Temperature Roll Stack - Pertengahan | 70 - 95 | °C |
| Roll Stack Temp - Bagian bawah | 65 - 90 | °C |
| Sumber GMD, terakhir diperbarui:11/27/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Geloy CR9020.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|