SabikXenoyX5630resin adalahCampuran PC/PET yang diisi mineral dengan stabilitas dimensi panas tinggi, penyusutan rendah dan CTE rendah, terutama untuk aplikasi cat
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 3.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 10 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4400 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 90 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 4200 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 56 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 3.2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4300 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4200 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 60 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 45 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 100 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 80 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 8 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 6 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 112 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 4.3E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.4E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 80°C, aliran | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C sampai 80°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, aliran | 4.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 6.8E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 138 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 112 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.35 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 266°C/5,0 kgf | 11 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.35 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.42 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 10 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:03/05/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu Nozzle | 260 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 270 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Sumber GMD, terakhir diperbarui:03/05/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X5630.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|