SabikGeloyCR8510resin adalahASA dengan kinerja paparan UV yang luar biasa untuk aplikasi eksterior dan interior.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 40 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 33 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1970 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 68 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2170 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 43 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 35 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 3.3 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 19 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2040 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 64 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2060 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 400 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 60 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 30 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 15 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 98 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 90 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 8.4E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, perkiraan maksimum | 98 | °C | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 102 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 105 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 88 | °C | ISO 75/Ae |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 89 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.08 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.8 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 6.3 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 11 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.07 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.2 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/10,0 kg | 6 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 260°C/5,0 kg | 10 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Faktor Dissipasi, 100 kHz | 0.018 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.026 | - | ASTM D 150 |
| Kekuatan dielektrik dalam minyak, 1,5 mm | 26.1 | kV/mm | IEC 60243-1 |
| Indeks Pelacakan Perbandingan | 600 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| Sinar UV, paparan air/pencelupan | F1 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:09/20/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 85 - 90 | °C |
| Waktu Pengeringan | 4 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.04 | % |
| Suhu Peleburan | 240 - 270 | °C |
| Suhu Nozzle | 220 - 255 | °C |
| Suhu depan - Zona 3 | 230 - 260 | °C |
| Tengah - Zona 2 Suhu | 220 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 215 - 250 | °C |
| Suhu Cetakan | 60 - 85 | °C |
| Tekanan Belakang | 0.3 - 1 | MPa |
| Kecepatan sekrup | 30 - 80 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.038 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:09/20/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |