SabikXenoyX5600HPresin adalahResin adalah campuran PBT/PC dengan kekuatan benturan yang baik dan ketahanan kimia untuk aplikasi yang sesuai dengan kontak makanan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 52 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 5 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 150 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2100 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 75 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2050 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2050 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2050 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Charpy Impact, tidak diukir, -30°C | NB | kJ/m2 | ISO 179/2C |
| Izod Dampak, bertanduk, 23°C | 750 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 600 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 80 | J | ASTM D 3763 |
| Izod Impact, tidak bergaris 80*10*4 -40°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 55 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 25 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 60 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 125 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 80 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 125 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 123 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.7 - 1.1 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 11 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.4 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 10 | cm3/10 menit | ISO 1133 |
| Viskositas peleburan, 260°C, 1500 detik-1 | 260 | Pa-s | ISO 11443 |
| Sumber GMD, terakhir diperbarui:03/14/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 255 - 270 | °C |
| Suhu Nozzle | 250 - 265 | °C |
| Suhu depan - Zona 3 | 250 - 270 | °C |
| Tengah - Zona 2 Suhu | 240 - 265 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 250 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:03/14/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X5600HP.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|