SabikXenoyX5410resin adalahResin PC + PET yang diisi mineral dengan stabilitas dimensi panas yang tinggi untuk sistem cat.pintu belakang, spoiler, rocker panel atau tankflaps
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 56 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 45 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 10 mm/menit | 56 | MPa | Metode S-Plastics - Jepang |
| Tekanan tarik, brk, tipe I, 10 mm/menit | 45 | MPa | Metode S-Plastics - Jepang |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 4.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 38.7 | % | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 10 mm/menit | 67 | % | Metode S-Plastics - Jepang |
| Tekanan tarik, brk, tipe I, 10 mm/menit | 100 | % | Metode S-Plastics - Jepang |
| Tensile Modulus, 5 mm/min | 3230 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 92 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2990 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 55 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 26 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4.1 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 12.1 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3190 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 93 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2700 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 87 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 82 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 54 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 7 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 7 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 137 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 129 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 109 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 134 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 60°C, aliran | 5.86E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 60°C, xflow | 7.05E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 80°C, aliran | 5.81E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 7.01E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pergi | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 137 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 140 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 128 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 105 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.65 - 0.75 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 0.2 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 19 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.26 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.42 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.14 | % | ISO 62 |
| Tingkat Aliran Peleburan, 250°C/2,16 kg | 0 | g/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 0 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 17 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:06/28/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 275 | °C |
| Suhu Nozzle | 255 - 270 | °C |
| Suhu depan - Zona 3 | 255 - 275 | °C |
| Tengah - Zona 2 Suhu | 250 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 265 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 50 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:06/28/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X5410.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|