SabikGeloyCR7020resin adalahASA copolymer. Profil / coextrusion lembaran atas ABS. ketahanan cuaca yang sangat baik, aliran / estetika yang baik dan dampak tinggi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 41 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 34 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1790 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 58 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1790 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 86 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 320 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 58 | J/m | ASTM D 256 |
| Efek Gardner (Prosedur B) | 10675 | J/m | ASTM D 4226 |
| Energi Total Dampak Instrumen, 23°C | 25 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 99 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 87 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 76 | °C | ASTM D 648 |
| HDT, 1,82 MPa, dipanaskan | 95 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 90 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 79 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.18E-05 | 1/°C | ASTM E 831 |
| CTE, -30°C sampai 0°C, aliran | 8.46E-05 | 1/°C | ASTM E 831 |
| CTE, 0°C sampai 100°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.06 | - | ASTM D 792 |
| Penyerapan air, keseimbangan, 23C | 0.55 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 7 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 13 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Berkilau, tidak bertekstur, 60 derajat | 95 | - | ASTM D 523 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 15.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 5.2 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.21 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.15 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.026 | - | ASTM D 150 |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
| Sinar UV, paparan air/pencelupan | F2 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:03/29/1999 | |||
| Parameter | ||
| Ekstrusi Profil | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 6 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.02 | % |
| Suhu Peleburan | 225 - 255 | °C |
| Barel - Zona 1 Suhu | 205 - 215 | °C |
| Barel - Zona 2 Suhu | 215 - 230 | °C |
| Barel - Zona 3 Suhu | 220 - 240 | °C |
| Barel - Zona 4 Suhu | 225 - 245 | °C |
| Suhu adaptor | 225 - 245 | °C |
| Suhu mati | 225 - 245 | °C |
| Suhu Kalibrator | 15 - 65 | °C |
| Sumber GMD, terakhir diperbarui:03/29/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |