SabikGeloyCR7010resin adalahCopolymer ASA untuk aplikasi ekstrusi lembaran.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3.2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 40 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1930 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 60 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1930 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 91 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 480 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 106 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 24 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, -30°C | 16 | J | ASTM D 3763 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 102 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 90 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 76 | °C | ASTM D 648 |
| HDT, 1,82 MPa, dipanaskan | 97 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 96 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 85 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.08E-04 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 50 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 50 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.06 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.5 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 3.7 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 260°C/5,0 kgf | 3.5 | g/10 menit | ASTM D 1238 |
| Optik | Nilai | Satuan | Standar |
| Berkilau, tidak bertekstur, 60 derajat | 95 | - | ASTM D 523 |
| Listrik | Nilai | Satuan | Standar |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.49 | mm | UL 94 |
| Sinar UV, paparan air/pencelupan | F2 | - | UL 746C |
| Sumber GMD, terakhir diperbarui:06/29/1998 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan | 220 - 245 | °C |
| Barel - Zona 1 Suhu | 180 - 225 | °C |
| Barel - Zona 2 Suhu | 190 - 230 | °C |
| Barel - Zona 3 Suhu | 205 - 240 | °C |
| Barel - Zona 4 Suhu | 210 - 245 | °C |
| Suhu adaptor | 210 - 245 | °C |
| Suhu mati | 210 - 245 | °C |
| Temperature Roll Stack - Atas | 70 - 100 | °C |
| Temperature Roll Stack - Pertengahan | 70 - 95 | °C |
| Roll Stack Temp - Bagian bawah | 65 - 90 | °C |
| Sumber GMD, terakhir diperbarui:06/29/1998 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Geloy CR7010.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|