SabikGeloyCR5020resin adalahASA berkilau rendah. terutama untuk capstock atas ABS dalam koekstrusi dan termoforming.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 40 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 31 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 24 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 2060 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 62 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2130 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 95 | - | ASTM D 785 |
| Tekanan tarik, hasil, 50 mm/menit | 40 | MPa | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 57 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 320 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 24 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 26 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 22 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 99 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 87 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 77 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 8.64E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.18E-05 | 1/°C | ASTM E 831 |
| Vicat Softening Temperature, Tingkat B/50 | 92 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 81 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.06 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 220°C/10,0 kgf | 7.1 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 220°C/10,0 kg | 7 | g/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:11/27/2001 | |||
| • Suhu tong harus dipertahankan hingga 150°C (300°F) | ||
| Parameter | ||
| Ekstrusi Lembar | Nilai | Satuan |
| Suhu Pengeringan | 80 - 90 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Minimal | 0.04 | % |
| Suhu Peleburan | 220 - 245 | °C |
| Barel - Zona 1 Suhu | 180 - 225 | °C |
| Barel - Zona 2 Suhu | 190 - 230 | °C |
| Barel - Zona 3 Suhu | 205 - 240 | °C |
| Barel - Zona 4 Suhu | 210 - 245 | °C |
| Suhu adaptor | 210 - 245 | °C |
| Suhu mati | 210 - 245 | °C |
| Temperature Roll Stack - Atas | 70 - 100 | °C |
| Temperature Roll Stack - Pertengahan | 70 - 95 | °C |
| Roll Stack Temp - Bagian bawah | 65 - 90 | °C |
| Sumber GMD, terakhir diperbarui:11/27/2001 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Geloy CR5020.pdf |
|