SabikXenoyX4700resin adalahXENOY X4700 adalah campuran PC+PBT berdampak tinggi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 50 mm/menit | 45 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2000 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 65 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1900 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -20°C | 40 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 35 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 40 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, bertanduk, 23°C | 50 | kJ/m2 | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 25 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.21 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 1.05E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.05E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 125 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 105 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 87 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.22 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Aliran Peleburan, 250°C/5,0 kg | 7 | g/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 6 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:03/04/2005 | |||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Suhu Peleburan (Parison) | 225 - 240 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Barel - Zona 1 Suhu | 225 - 240 | °C |
| Barel - Zona 2 Suhu | 225 - 240 | °C |
| Barel - Zona 3 Suhu | 230 - 250 | °C |
| Suhu akumulator | 220 - 240 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Suhu mati | 225 - 240 | °C |
| Sumber GMD, terakhir diperbarui:03/04/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X4700.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|