SabikXenoyX4000BMresin adalahUV stabil, kekuatan peleburan tinggi untuk thermoforming, ekstrusi atau blow molding dari aplikasi eksterior otomotif besar.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 50 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 51 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 110 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 80 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2200 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 52 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 120 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 60 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 715 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 530 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 50 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 50 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 20 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 50 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 88 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 7.6E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.6E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 121 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 80 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.19 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.8 - 1 | % | Metode S-Plastics |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Sumber GMD, terakhir diperbarui:06/16/2005 | |||
| Parameter | ||
| Pengeboran dengan Ekstrusi | Nilai | Satuan |
| Suhu Pengeringan | 95 - 100 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.01 - 0.02 | % |
| Kandungan Kelembaban Minimal | 0.02 | % |
| Suhu Peleburan (Parison) | 240 - 250 | °C |
| Barel - Zona 1 Suhu | 235 - 245 | °C |
| Barel - Zona 2 Suhu | 235 - 245 | °C |
| Barel - Zona 3 Suhu | 235 - 245 | °C |
| Barel - Zona 4 Suhu | 235 - 245 | °C |
| Adaptor - Zona 5 Suhu | 235 - 245 | °C |
| Kepala - Zona 6 - Suhu puncak | 235 - 245 | °C |
| Kepala - Zona 7 - Suhu bawah | 235 - 245 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Suhu mati | 240 - 250 | °C |
| Sumber GMD, terakhir diperbarui:06/16/2005 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X4000BM.pdf |
|