SabikXenoyX3515resin adalahFlame Retardant, Impact Modified, Opaque, Dirancang untuk aplikasi luar ruangan telekomunikasi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 52 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4.3 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 44 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2150 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 72 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1860 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 47 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4.1 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 58 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1960 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 71 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1890 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 747 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -20°C | 694 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 450 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 427 | J/m | ASTM D 256 |
| Dampak Instrumen, Energi @ puncak, -20°C | 56 | J | ASTM D 3763 |
| Energi dampak instrumen @ puncak, -30 | 70 | J | ASTM D 3763 |
| Energi Dampak Instrumen @ puncak, -40°C | 74 | J | ASTM D 3763 |
| Energi Total Dampak Instrumen, 23°C | 62 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 53 | kJ/m2 | ISO 180/1A |
| Izod Impact, bernotas 80*10*4 0°C | 47 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -10°C | 43 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 40 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 53 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 110 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 74 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 123 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 95 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.8E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 9.8E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 120 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 122 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 114 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 88 | °C | ISO 75/Af |
| Indeks suhu relatif, Elec | 75 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 75 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 75 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.3 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.8 - 1 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.8 - 1 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/2,16 kgf | 4.8 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 15.1 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 265°C/2,16kg | 8 | g/10 menit | ASTM D 1238 |
| Tingkat Aliran Peleburan, 266°C/5,0 kgf | 26.7 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Aliran Peleburan, 250°C/2,16 kg | 4 | g/10 menit | ISO 1133 |
| Tingkat Aliran Peleburan, 250°C/5,0 kg | 15 | g/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 250°C/2,16 kg | 4 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 13 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 7 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 265°C/5,0 kg | 23 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 2 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 0 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 1.47 | mm | UL 94 oleh GE |
| Sesuai UL, 94-5VA rating (3) (((4) | 2.99 | mm | UL 94 oleh GE |
| Indeks Oksigen (LOI) | 28 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:08/22/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 4 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 265 | °C |
| Suhu Nozzle | 245 - 260 | °C |
| Suhu depan - Zona 3 | 250 - 265 | °C |
| Tengah - Zona 2 Suhu | 245 - 260 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 255 | °C |
| Suhu Cetakan | 50 - 75 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 80 | % |
| Kedalaman ventilasi | 0.025 - 0.038 | mm |
| Sumber GMD, terakhir diperbarui:08/22/2006 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X3515.pdf |
|