SabikXenoyX3108UVresin adalahTidak diperkuat, UV-stabil, tahan api, dampak dimodifikasi PBT + PC dengan V0 pada ketebalan 0,8mm.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 52 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 42 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 26 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2150 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 78 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2020 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 50 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 40 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 5 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 30 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 2200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 80 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2000 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 522 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 158 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 60 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 45 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 10 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 45 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 148 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 88 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 80°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | lulus | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 145 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 150 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 85 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 120 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 1.1 - 1.2 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 9.3 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.34 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+16 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | 1.E+16 | Ohm | ASTM D 257 |
| Resistivitas Volume | >1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 18 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 3 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.007 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 225 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-0 (3) | 0.75 | mm | UL 94 oleh GE |
| Sesuai UL, 94-5VA rating (3) (((4) | 2.5 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 960°C, melewati pada | 1 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 30 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:11/06/2006 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 250 - 270 | °C |
| Suhu Nozzle | 240 - 260 | °C |
| Suhu depan - Zona 3 | 245 - 265 | °C |
| Tengah - Zona 2 Suhu | 240 - 255 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 245 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 40 - 100 | °C |
| Sumber GMD, terakhir diperbarui:11/06/2006 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy X3108UV.pdf |
|