SabikXenoyHX6600HPresinadalah campuran semi-kristalin berbasis PBT dengan aliran seimbang dan properti dampak. Resistensi kimia yang lebih baik terhadap disinfektan laboratorium dan bahan kimia untuk aplikasi kesehatan dan perumahan.Manajemen perubahan perawatan kesehatan, biocompatible (ISO10993 atau USP Kelas VI).
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 43 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 35 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 4 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 150 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 1900 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 43 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1900 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 44 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 37 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 100 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 1900 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 64 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 1800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 800 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 750 | J/m | ASTM D 256 |
| Dampak Multiaxial | 100 | J | ISO 6603 |
| Energi Total Dampak Instrumen, 23°C | 100 | J | ASTM D 3763 |
| Izod Impact, tidak bergaris 80*10*4 -40°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 65 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 20 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 70 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 117 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 60 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 60°C, aliran | 1.3E-04 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 117 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 120 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 95 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 60 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.21 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 1.2 - 1.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 250°C/5,0 kgf | 11 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.21 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.4 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.05 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 250°C/5,0 kg | 10 | cm3/10 menit | ISO 1133 |
| Viskositas peleburan, 260°C, 1500 detik-1 | 210 | Pa-s | ISO 11443 |
| Sumber GMD, terakhir diperbarui:03/14/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 90 - 100 | °C |
| Waktu Pengeringan | 2 - 4 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 255 - 270 | °C |
| Suhu Nozzle | 250 - 265 | °C |
| Suhu depan - Zona 3 | 250 - 270 | °C |
| Tengah - Zona 2 Suhu | 240 - 265 | °C |
| Bagian belakang - Zona 1 Suhu | 230 - 250 | °C |
| Suhu Hopper | 40 - 60 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:03/14/2008 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy HX6600HP.pdf |
|