SabikXenoyEXXY0174resin adalah7% PC/PET dengan aliran mudah diisi kaca
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, hasil, 5 mm/menit | 75 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 75 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3850 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 118 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3400 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | 20 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1U |
| Termal | Nilai | Satuan | Standar |
| CTE, -40°C sampai 40°C, aliran | 4.7E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/120 | 145 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 127 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Kepadatan | 1.29 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 265°C/2,16 kg | 15 | cm3/10 menit | ISO 1133 |
| Viskositas peleburan, 280°C, 1500 detik-1 | 180 | Pa-s | ISO 11443 |
| Sumber GMD, terakhir diperbarui:10/10/2008 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 265 - 275 | °C |
| Suhu Nozzle | 260 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 270 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 100 | °C |
| Sumber GMD, terakhir diperbarui:10/10/2008 | ||