SabikXenoy9159Uresin adalahPanas tinggi, paduan poliester / polikarbonat dampak tinggi.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 89 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2240 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 747 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 110 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 60°C, aliran | 9.72E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.9 | % | Metode S-Plastics |
| Sumber GMD, terakhir diperbarui:06/18/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 120 | °C |
| Waktu Pengeringan | 3 - 6 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Suhu Peleburan | 255 - 275 | °C |
| Suhu Cetakan | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui:06/18/1999 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy 9159U.pdf |
|