SabikXenoy6380Uresin adalah30% kaca diperkuat, kualitas UV stabil, yang menggabungkan kekakuan tinggi dengan fleksibilitas yang lebih baik. The combination of mechanical properties at high and low temperatures and chemical resistance makes XENOY 6380U a suitable material for a wide range of demanding applications where safety is a primary considerationKarakteristik gloss material adalah keuntungan tambahan untuk bagian penampilan di industri peralatan.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 100 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 100 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 2 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 8200 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 140 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 7000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 2 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 2 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 8400 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 145 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 7200 | MPa | ISO 178 |
| Kekerasan, H358/30 | 115 | MPa | ISO 2039-1 |
| Kekerasan, Rockwell R | 110 | - | ISO 2039-2 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 650 | J/m | ASTM D 4812 |
| Izod Impact, tidak diukir, -30°C | 600 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 60 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 7 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 40 | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 10 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m2 | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | 40 | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 165 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 2.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 1.E-04 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.19 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 80°C, aliran | 2.3E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 1.3E-04 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 180 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 180 | °C | ISO 306 |
| HDT/Bf, 0,45 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Bf |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 180 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.51 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.3 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 266°C/1,2 kgf | 13 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.51 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.5 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.15 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 265°C/1,2 kg | 9 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | >1.E+14 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 20 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 4.2 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 4 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.002 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.02 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 300 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.5 | mm | UL 94 |
| UL Diakui, 94HB Kelas Api Nilai ke-2 (3) | 3 | mm | UL 94 |
| Glow Wire Flammability Index 750°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Sumber GMD, terakhir diperbarui:05/04/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 - 120 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 265 - 285 | °C |
| Suhu Nozzle | 260 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 250 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 240 - 270 | °C |
| Suhu Hopper | 60 - 80 | °C |
| Suhu Cetakan | 60 - 110 | °C |
| Sumber GMD, terakhir diperbarui:05/04/2007 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy 6380U.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|