SabikUltem 9085resin adalahCampuran Polyetherimide aliran tinggi. Memenuhi FAR 25.853 dan OSU 65/65 dengan toksisitas rendah, asap dan api evolusi.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 84 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 74 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 72 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3440 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 138 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2920 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 88 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 71 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6.7 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 50 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3050 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 90 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2750 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 115 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 0 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 13 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 0 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 0 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 0 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 153 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 0.E+00 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, xflow | 0.E+00 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 150°C, aliran | 0.E+00 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 0.E+00 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 0 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 173 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 152 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 295°C/6,6 kgf | 8.9 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.34 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.39 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.17 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 65 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| FAR 25.853 A/B | < 5 | - | FAR 25.853 |
| OSU total pelepasan panas (tes 2 menit) | 16 | kW-menit/m2 | FAR 25.853 |
| Kecepatan pelepasan panas puncak OSU (tes 5 menit) | 36 | kW/m2 | FAR 25.853 |
| Vertikal Burn a (60s) melewati di | 2 | detik | FAR 25.853 |
| Indeks Oksigen (LOI) | 49 | % | ASTM D 2863 |
| Sumber GMD, terakhir diperbarui:01/19/2007 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 330 - 350 | °C |
| Suhu Nozzle | 330 - 350 | °C |
| Suhu depan - Zona 3 | 330 - 350 | °C |
| Tengah - Zona 2 Suhu | 325 - 345 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 120 - 150 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/19/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem 9085.pdf |
|