SabikUltem 9011resin adalahTransparan, Polyetherimide aliran tinggi (Tg 217C). ECO Conforming. Kelayakan proses yang ditingkatkan untuk ekstrusi Serat.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 105 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3520 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 1175 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 219 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 197 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 207 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 199 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 17.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 25 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 44 | % | ASTM D 2863 |
| Sumber GMD, terakhir diperbarui:03/31/2005 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:03/31/2005 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem 9011.pdf |
|