SabikUltem 6601resin adalah5% Isi serat kaca, campuran Copolymer Polyetherimide aliran standar.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 15 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3720 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 176 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3990 | MPa | ASTM D 790 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 215 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.32 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 367°C/6,6 kgf | 10.5 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 380 - 405 | °C |
| Suhu Nozzle | 375 - 400 | °C |
| Suhu depan - Zona 3 | 380 - 405 | °C |
| Tengah - Zona 2 Suhu | 370 - 395 | °C |
| Bagian belakang - Zona 1 Suhu | 360 - 380 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 | ||
Untuk informasi lebih lanjut silahkan unduh lembar data | |
 | S-Plastics Ultem 6601.pdf |