SabikUltem 4211resin adalah20% Isi serat kaca dan PTFE, aliran standar Polyetherimide (Tg 217C).
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 129 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 193 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 7100 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, Reverse Notched, 3,2 mm | 437 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 212 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.48 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 10.3 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 10 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 370 | °C |
| Suhu Nozzle | 350 - 370 | °C |
| Suhu depan - Zona 3 | 350 - 370 | °C |
| Tengah - Zona 2 Suhu | 345 - 365 | °C |
| Bagian belakang - Zona 1 Suhu | 340 - 360 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 | ||