SabikUltem 4000resin adalahSerat kaca, PTFE, dan Grafit diisi, aliran standar Polyetherimide (Tg 217C).
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 82 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 1.2 | % | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 113 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 137 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 8820 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 85 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 33 | mg/1000cy | ASTM D 1044 |
| Batas PV, 0,51 m/s | 2.1 | MPa-m/s | Metode S-Plastics |
| K-faktor xE-10, PV = 2000 psi-fpm vs Baja | 62 | - | Metode S-Plastics |
| K-faktor xE-10, PV = 2000 psi-fpm vs Self | 1900 | - | Metode S-Plastics |
| Koefisien gesekan pada baja, statis | 0.25 | - | ASTM D 1894 |
| Koefisien gesekan pada baja,kinetik | 0.24 | - | ASTM D 1894 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 160 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 64 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 170 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 233 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 212 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 1.62E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, aliran | 1.62E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 105 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 105 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.67 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.11 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.3 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 3.1 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.83 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 10 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 370 | °C |
| Suhu Nozzle | 350 - 370 | °C |
| Suhu depan - Zona 3 | 350 - 370 | °C |
| Tengah - Zona 2 Suhu | 345 - 365 | °C |
| Bagian belakang - Zona 1 Suhu | 340 - 360 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem 4000.pdf |
|