SabikUltem XH6050Fresin adalahTransparent, enhanced flow Polyetherimidesulfone copolymer (Tg 247C). ECO Conform. US FDA Compliant. Resin tunduk pada UU Pengendalian Perdagangan AS (15CFR Bab VII, Bagian 774).
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 25 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3510 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 1,3 mm/menit, rentang 50 mm | 159 | MPa | ASTM D 790 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 155 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3170 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3100 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 95 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 78 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 8.5 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 16.8 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3110 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 123 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3080 | MPa | ISO 178 |
| Kekerasan, H358/30 | 140 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | NB | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 69 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 74 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, Unnotch Edge 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | NB | kJ/m2 | ISO 179/1eU |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 242 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 222 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 217 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 237 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 230 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 5.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 5.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.22 | W/m-°C | ASTM E 1530 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 242 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 238 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 228 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.3 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 367°C/6,6 kgf | 12.5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.3 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.75 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.6 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 8 | cm3/10 menit | ISO 1133 |
| Optik | Nilai | Satuan | Standar |
| Transmisi Cahaya | 58 | % | ASTM D 1003 |
| Kabut | 2 | % | ASTM D 1003 |
| Listrik | Nilai | Satuan | Standar |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 17 | kV/mm | ASTM D 149 |
| Faktor Dissipasi, 50/60 Hz | 0.025 | - | IEC 60250 |
| Faktor Dissipasi, 100 Hz | 0.008 | - | IEC 60250 |
| Faktor Dissipasi, 1 kHz | 0.001 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.007 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 175 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Suhu pembakaran kawat bercahaya, 3,0 mm | 850 | °C | IEC 60695-2-13 |
| Indeks Oksigen (LOI) | 45 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:12/14/2004 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 380 - 405 | °C |
| Suhu Nozzle | 375 - 400 | °C |
| Suhu depan - Zona 3 | 380 - 405 | °C |
| Tengah - Zona 2 Suhu | 370 - 395 | °C |
| Bagian belakang - Zona 1 Suhu | 360 - 380 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/14/2004 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem XH6050F.pdf |
|