SabikUltem UR1100Bresin adalahAliran standar, polietherimide tahan api (Tg 217C).
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 70 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 50 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3720 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3720 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 10 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 140 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 37 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 40 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 219 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 194 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.26 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 210 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 205 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 185 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.36 | - | ASTM D 792 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.4 - 0.6 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.4 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 8.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.37 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.65 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 340°C/5,0 kg | 12 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:07/12/2006 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 360 - 400 | °C |
| Suhu Nozzle | 360 - 400 | °C |
| Suhu depan - Zona 3 | 370 - 410 | °C |
| Tengah - Zona 2 Suhu | 360 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 340 - 380 | °C |
| Suhu Hopper | 80 - 100 | °C |
| Suhu Cetakan | 140 - 180 | °C |
| Sumber GMD, terakhir diperbarui:07/12/2006 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem UR1100B.pdf |
|