SabikUltem STM1500resin adalahSiloxane polyetherimide block copolymer, kabel dan kawat, kekuatan dan fleksibilitas.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 28 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 100 | % ASTM D 638 | |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 380 | MPa | ASTM D 790 |
| Taber Abrasion, CS-17, 1 kg | 26 | mg/1000cy | ASTM D 1044 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.18 | - | ASTM D 792 |
| Penyerapan Kelembaban (est) | < 0 | % ASTM D 570 | |
| Tingkat Aliran Peleburan, 295°C/6,6 kgf | 12 | g/10 menit | ASTM D 1238 |
| Matriks Tg | 168 | °C | DMA |
| Kandungan Halogen | 0 | % Metode S-Plastics | |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 4.1E+16 | Ohm-cm | ASTM D 257 |
| Resistensi Permukaan | >1.E+15 | Ohm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 16.1 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16.3 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 50/60 Hz | 3.01 | - | ASTM D 150 |
| Permittivitas relatif, 100 kHz | 2.7 | - | ASTM D 150 |
| Faktor Dissipasi, 50/60 Hz | 0.01 | - | ASTM D 150 |
| Faktor Dissipasi, 100 kHz | 0.0056 | - | ASTM D 150 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Kecepatan pelepasan panas puncak OSU (tes 5 menit) | 140 | kW/m2 | FAR 25.853 |
| Indeks Oksigen (LOI) | 46 | % ASTM D 2863 | |
| WIRE AND CABLE - UL 1581 diuji pada kawat 2,0mm dengan 0,12mmx20 stranded tembaga |
Nilai | Satuan | Standar |
| Ketebalan dinding kabel | 10 | Mil | - |
| Kekuatan tarik (Wire/Cable), pecah | - | - | S-Plastics (UL1561) |
| Awalnya | 37 | MPa | - |
| Usia 1 minggu pada 135°C | 38 | MPa | - |
| Kekuatan Tarikan | 102 | % | - |
| Perpanjangan Tensile (Wire/Cable), putus | - | - | S-Plastics (UL1561) |
| Awalnya | 400 | % | - |
| Usia 1 minggu pada 135°C | 370 | % | - |
| Retensi Perpanjangan Tekanan | 94 | % | - |
| Korosifitas pembakaran | Nilai | Satuan | Standar |
| Korosi, 1 jam (2500 angstroms maksimal) | 40 | Angstrom | ASTM E5.2170 |
| Korosi, 24 jam | 122 | Angstrom | ASTM E5.2170 |
| Korosi, 6 hari | 183 | Angstrom | ASTM E5.2170 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 105 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 300 - 320 | °C |
| Suhu Nozzle | 300 - 320 | °C |
| Suhu depan - Zona 3 | 295 - 315 | °C |
| Tengah - Zona 2 Suhu | 295 - 315 | °C |
| Bagian belakang - Zona 1 Suhu | 295 - 315 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 100 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem STM1500.pdf |
|