SabikUltem SILTEM-STM1500resin adalahsebuah kopolymer siloksana-polieterimida yang fleksibel untuk lapisan kabel dan kawat.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 60 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 20 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 25 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 15 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 110 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 590 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 20 | MPa | ISO 178 |
| Tekanan lentur, istirahat, 2 mm/menit | 18 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 470 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 25 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 15 | kJ/m2 | ISO 180/1A |
| Termal | Nilai | Satuan | Standar |
| CTE, 23°C sampai 80°C, aliran | 1.1E-04 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 80°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 75°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat B/50 | 75 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 78 | °C | ISO 306 |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 1.2 - 1.4 | % | Metode S-Plastics |
| Kepadatan | 1.18 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 0.12 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 320°C/2,16 kg | 8 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 4.7E+14 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 19 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 100 Hz | 3 | - | IEC 60250 |
| Faktor Dissipasi, 100 Hz | 0.0091 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 175 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 100 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Sesuai UL, Kelas Api 94V-1 (3)(4) | 1.6 | mm | UL 94 oleh GE |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 48 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui: 03/26/1996 | |||
| Ekstrusi Profil | Nilai | Satuan |
| Suhu Pengeringan | 105 - 110 | °C |
| Waktu Pengeringan | 5 - 7 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 285 - 320 | °C |
| Barel - Zona 1 Suhu | 280 - 290 | °C |
| Barel - Zona 2 Suhu | 300 - 310 | °C |
| Barel - Zona 3 Suhu | 310 - 320 | °C |
| Barel - Zona 4 Suhu | 310 - 325 | °C |
| Suhu Hopper | 60 - 100 | °C |
| Suhu adaptor | 315 - 325 | °C |
| Suhu mati | 300 - 320 | °C |
| Suhu Kalibrator | 60 - 80 | °C |
| Sumber GMD, terakhir diperbarui: 03/26/1996 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem SILTEM STM1500.pdf |
|