SabikUltem MD141resin adalahTransparan, aliran standar Polyetherimide (Tg 217C). ECO Conform. UL94 V0 dan 5VA daftar. US FDA dan EU Food Contact sesuai.
| Mekanis | Nilai | Satuan | Standar |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | Metode S-Plastics |
| Tekanan tarik, hasil, 50 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Kekerasan, H358/30 | 140 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Charpy Impact, bertanduk, 23°C | 10 | kJ/m2 | ISO 179/2C |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Konduktivitas Termal | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 170 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 170 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 170 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 13 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 33 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.0005 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.006 | - | IEC 60250 |
| Faktor Dissipasi, 2450 MHz | 0.0025 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 150 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 100 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 47 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:02/17/2006 | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 150 | °C | |
| Waktu Pengeringan | 4 - 6 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 370 - 410 | °C | |
| Suhu Nozzle | 350 - 405 | °C | |
| Suhu depan - Zona 3 | 360 - 415 | °C | |
| Tengah - Zona 2 Suhu | 350 - 405 | °C | |
| Bagian belakang - Zona 1 Suhu | 340 - 395 | °C | |
| Suhu Hopper | 80 - 120 | °C | |
| Suhu Cetakan | 140 - 180 | °C | |
| Sumber GMD, terakhir diperbarui:02/17/2006 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem MD141.pdf |
|