SabikXenoy5220resin adalahTidak diperkuat, campuran polimer berbasis polikarbonat, ketahanan kimia dan dampak yang sangat baik.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 53 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 58 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 120 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 84 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 2040 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 112 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 3204 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 710 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -40°C | 299 | J/m | ASTM D 256 |
| Gardner, 23°C | 54 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 106 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 98 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 7.74E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, aliran | 9.E-05 | 1/°C | ASTM E 831 |
| CTE, 60°C sampai 138°C, aliran | 1.1E-04 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 75 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 75 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 75 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.21 | - | ASTM D 792 |
| Volume Spesifik | 0.82 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.12 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.8 - 1 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.8 - 1 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 2.4E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 20.7 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 2.99 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 3.04 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.019 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 3 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 0 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 1 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94HB Flame Class Rating (3) | 1.47 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 275 | °C |
| Suhu Nozzle | 255 - 270 | °C |
| Suhu depan - Zona 3 | 255 - 275 | °C |
| Tengah - Zona 2 Suhu | 250 - 270 | °C |
| Bagian belakang - Zona 1 Suhu | 245 - 265 | °C |
| Suhu Cetakan | 65 - 90 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 50 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy 5220.pdf |
|