SabikUltem 2300Rresin adalah30% Serat Kaca diisi, aliran standar Polyetherimide (Tg 217C) dengan pelepasan cetakan internal.
| Sifat-sifat khas(1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 168 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 158 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 3 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 9300 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 227 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 8960 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 114 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 427 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 85 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 491 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 227 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 212 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 210 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 1.98E-05 | 1/°C | ASTM E 831 |
| Indeks suhu relatif, Elec | 180 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 170 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 180 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.51 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.16 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.9 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.2 - 0.4 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 5.3 | g/10 menit | ASTM D 1238 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 3.E+16 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 1,6 mm | 24.8 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 30.3 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 1 kHz | 3.7 | - | ASTM D 150 |
| Faktor Dissipasi, 1 kHz | 0.0015 | - | ASTM D 150 |
| Faktor Dissipasi, 2450 MHz | 0.0053 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 4 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.25 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 1.21 | mm | UL 94 |
| Indeks Oksigen (LOI) | 50 | % | ASTM D 2863 |
| Densitas Asap, Api, Ds 4 min | 1.6 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:12/29/1999 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:12/29/1999 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem 2300R.pdf |
|