SabikUltem MD131resin adalahTransparan, Polyimide aliran tinggi (Tg 217C).
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 105 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 167 | MPa | ASTM D 790 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3550 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3520 | MPa | ASTM D 790 |
| Kekerasan, Rockwell M | 109 | - | ASTM D 785 |
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | ASTM D 1044 |
| Tekanan tarik, hasil, 50 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Kekerasan, H358/30 | 140 | MPa | ISO 2039-1 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 32 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 35 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 1174 | J/m | ASTM D 256 |
| Gardner, 23°C | 33 | J | Metode S-Plastics |
| Energi Total Dampak Instrumen, 23°C | 33 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 5 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 5 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 218 | °C | ASTM D 1525 |
| HDT, 0,45 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 197 | °C | ASTM D 648 |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 207 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 198 | °C | ASTM D 648 |
| CTE, -40°C sampai 150°C, aliran | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.22 | W/m-°C | ASTM C 177 |
| Konduktivitas Termal | 0.21 | W/m-°C | ISO 8302 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Uji tekanan bola, 125°C +/- 2°C | Pas | - | IEC 60695-10-2 |
| Vicat Softening Temperature, Tingkat A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 190 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.25 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 1.25 | % | ASTM D 570 |
| Penyusutan jamur pada batang tarik, aliran (2) | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 17.8 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 340°C/5,0 kg | 13 | cm3/10 menit | ISO 1133 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 25 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 1,6 mm | 32.6 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 27.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 1 kHz | 3.15 | - | ASTM D 150 |
| Faktor Dissipasi, 1 kHz | 0.0013 | - | ASTM D 150 |
| Faktor Dissipasi, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Resistivitas Volume | 1.E+15 | Ohm-cm | IEC 60093 |
| Resistensi permukaan, ROA | >1.E+15 | Ohm | IEC 60093 |
| Kekuatan Dielektrik, dalam minyak, 0,8 mm | 33 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 25 | kV/mm | IEC 60243-1 |
| Kekuatan dielektrik, dalam minyak, 3,2 mm | 16 | kV/mm | IEC 60243-1 |
| Permittivitas relatif, 50/60 Hz | 2.9 | - | IEC 60250 |
| Permittivitas Relatif, 1 MHz | 2.9 | - | IEC 60250 |
| Faktor Dissipasi, 50/60 Hz | 0.0005 | - | IEC 60250 |
| Faktor Dissipasi, 1 MHz | 0.006 | - | IEC 60250 |
| Faktor Dissipasi, 2450 MHz | 0.0025 | - | IEC 60250 |
| Indeks Pelacakan Perbandingan | 150 | V | IEC 60112 |
| Indeks Pelacakan Perbandingan, M | 100 | V | IEC 60112 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 44 | % | ASTM D 2863 |
| Glow Wire Flammability Index 960°C, melewati pada | 3.2 | mm | IEC 60695-2-12 |
| Indeks Oksigen (LOI) | 47 | % | ISO 4589 |
| Sumber GMD, terakhir diperbarui:02/02/2006 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:02/02/2006 | ||
Tersedia di stok dengan harga yang menguntungkan
1.1000 seri
1000, MI9.0; 1010, MI18.0; Hu1000, kelas medis.
2Seri 2000, tambahkan GF
2100, tambahkan 10% GF, MI 7.0;
2110, tambahkan 10% GF, MI 11.0;
2200, tambahkan 20% GF, MI 6.0;
2210, tambahkan 20% GF, MI 8.4;
2300, tambahkan 30% GF, MI 5.0;
2310, tambahkan 30% GF, MI 7.6;
3. lainnya
MD130, MD131, AUT195, ATX200, dll.
Dalam beberapa tahun terakhir, kami telah mengembangkan pasar domestik dan secara aktif mengeksplorasi pasar luar negeri.Hingga saat ini, kami telah menyediakan produk dan layanan berkualitas tinggi untuk lebih dari 1.000 pelanggan di berbagai industri, termasuk: elektronik dan peralatan listrik, medis, makanan,elektronik otomotif, komunikasi optoelektronik, energi fotovoltaik baru, pengolahan air, transportasi dan industri lainnya.
Samtion Chemical memasok plastik teknik dan bahan khusus yang dimodifikasi dari S-Plastics dan merek lain. Produk asli kami dijamin,dengan kualifikasi lengkap dan kapasitas pasokan yang unggul dan keuntungan harga.
Setiap batch produk kami adalah subjek inspeksi kualitas yang ketat untuk memastikan pasokan asli. Semua produk memiliki sertifikat MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA!!
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Ultem MD131.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|