SabikUltem LTX921Aresin adalahBerbasis daur ulang pasca-industri, 20% isi serat kaca, campuran Polyetherimide aliran tinggi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 131 | MPa | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 6960 | MPa | ASTM D 638 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 193 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 7230 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 427 | J/m | ASTM D 256 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 198 | °C | ASTM D 648 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.44 | - | ASTM D 792 |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 10 | g/10 menit | ASTM D 1238 |
| Sumber GMD, terakhir diperbarui:01/04/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 340 - 360 | °C |
| Suhu Nozzle | 330 - 355 | °C |
| Suhu depan - Zona 3 | 340 - 360 | °C |
| Tengah - Zona 2 Suhu | 325 - 350 | °C |
| Bagian belakang - Zona 1 Suhu | 315 - 340 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/04/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |