SabikUltem LTX300Bresin adalahCampuran Polyetherimide aliran standar dengan toksisitas rendah, asap, dan evolusi api.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 96 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 88 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3340 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 144 | MPa | ASTM D 790 |
| Tekanan lentur, brk, 2,6 mm/menit, rentang 100 mm | 141 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3200 | MPa | ASTM D 790 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 80 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 2136 | J/m | ASTM D 256 |
| Gardner, 23°C | 35 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 190 | °C | ASTM D 648 |
| Indeks suhu relatif, Elec | 140 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 115 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 140 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.3 - 0.5 | % | Metode S-Plastics |
| Penyusutan jamur, xflow, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 295°C/6,6 kgf | 1.6 | g/10 menit | ASTM D 1238 |
| Kandungan Halogen | 0 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistensi busur, Tungsten {PLC} | 6 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 0 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 3 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 0 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.76 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:01/13/2000 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 135 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 12 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 330 - 355 | °C |
| Suhu Nozzle | 325 - 350 | °C |
| Suhu depan - Zona 3 | 330 - 355 | °C |
| Tengah - Zona 2 Suhu | 320 - 345 | °C |
| Bagian belakang - Zona 1 Suhu | 310 - 330 | °C |
| Suhu Cetakan | 95 - 135 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:01/13/2000 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem LTX300B.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|