SabikXenoy2235resin adalahTidak diperkuat, paduan PC + PET transparan. ketahanan kimia, stabilitas dimensi dan kinerja mekanik. versi aliran mudah 2230.
| Properti Tipikal (1) | |||
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 50 mm/menit | 55 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 50 mm/menit | 75 | % | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 82 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 1890 | MPa | ASTM D 790 |
| Kekerasan, Rockwell R | 115 | - | ASTM D 785 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 640 | J/m | ASTM D 256 |
| Gardner, 23°C | 54 | J | ASTM D 3029 |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 129 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 121 | °C | ASTM D 648 |
| CTE, -40°C sampai 95°C, aliran | 8.46E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 95°C, xflow | 8.82E-05 | 1/°C | ASTM E 831 |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.22 | - | ASTM D 792 |
| Volume Spesifik | 0.82 | cm3/g | ASTM D 792 |
| Penyerapan air, 24 jam | 0.14 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 0.6 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.6 - 0.9 | % | Metode S-Plastics |
| Penyusutan jamur pada batang tarik, xflow (2) | 0.6 - 0.9 | % | Metode S-Plastics |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+15 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 3,2 mm | 16.8 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 100 Hz | 2.9 | - | ASTM D 150 |
| Permittivitas Relatif, 1 MHz | 2.8 | - | ASTM D 150 |
| Faktor Dissipasi, 100 Hz | 0.002 | - | ASTM D 150 |
| Faktor Dissipasi, 1 MHz | 0.001 | - | ASTM D 150 |
| Sumber GMD, terakhir diperbarui:01/05/2000 | |||
| Parameter | ||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 110 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 8 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 260 - 280 | °C |
| Suhu Nozzle | 255 - 275 | °C |
| Suhu depan - Zona 3 | 260 - 280 | °C |
| Tengah - Zona 2 Suhu | 255 - 275 | °C |
| Bagian belakang - Zona 1 Suhu | 250 - 270 | °C |
| Suhu Cetakan | 65 - 95 | °C |
| Tekanan Belakang | 0.3 - 0.6 | MPa |
| Kecepatan sekrup | 50 - 80 | rpm |
| Menembak untuk ukuran silinder | 50 - 80 | % |
| Kedalaman ventilasi | 0.013 - 0.02 | mm |
| Sumber GMD, terakhir diperbarui:01/05/2000 | ||
Produk terkait lainnya yang kami rekomendasikan:
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Xenoy 2235.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|