SabikUltem HU2100resin adalah10% Serat kaca diisi, aliran standar Polyimide (Tg 217C). FDA AS dan Kontak Makanan Eropa disetujui. Untuk perangkat medis dan aplikasi farmasi.biocompatible (ISO 10993 atau USP Kelas VI).
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 114 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 115 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 6 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 6 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 4680 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 160 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 5500 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 115 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 4 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 4 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 4500 | MPa | ISO 527 |
| Tekanan lentur, istirahat, 2 mm/menit | 185 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 4500 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 53 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 10 | J | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | 30 | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | 30 | kJ/m2 | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 7 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 223 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 3,2 mm, tidak diiris | 205 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 3.24E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 6.E-05 | 1/°C | ASTM E 831 |
| CTE, 23°C sampai 150°C, aliran | 2.6E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 6.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 217 | °C | ISO 306 |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae |
| Indeks suhu relatif, Elec | 170 | °C | UL 746B |
| Indeks suhu relatif, Mech w/impact | 170 | °C | UL 746B |
| Indeks suhu relatif, Mech tanpa dampak | 170 | °C | UL 746B |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.34 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.6 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 200°C/3,8 kgf | 5 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.34 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.6 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 9 | cm3/10 menit | ISO 1133 |
| Sumber GMD, terakhir diperbarui:06/21/2007 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 370 - 410 | °C |
| Suhu Nozzle | 350 - 405 | °C |
| Suhu depan - Zona 3 | 360 - 415 | °C |
| Tengah - Zona 2 Suhu | 350 - 405 | °C |
| Bagian belakang - Zona 1 Suhu | 340 - 395 | °C |
| Suhu Hopper | 80 - 120 | °C |
| Suhu Cetakan | 140 - 180 | °C |
| Sumber GMD, terakhir diperbarui:06/21/2007 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |