SabikUltem HU1110resin adalahEnhanced flow Polyetherimide (Tg 217C). ECO Conform. Untuk perangkat medis dan aplikasi farmasi. Manajemen perubahan perawatan kesehatan, biokompatibel (ISO 10993 atau USP Kelas VI),Cocok untuk kontak makanan. EtO dan uap sterilisasi. daftar NSF 51,
yang sesuai dengan warna yang dikenal.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 85 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 70 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3720 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 174 | MPa | ASTM D 790 |
| Tekanan lentur, yld, 2,6 mm/menit, rentang 100 mm | 165 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3420 | MPa | ASTM D 790 |
| Flexural Modulus, 2,6 mm/menit, rentang 100 mm | 3720 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 110 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3500 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 140 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 56 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | - | J/m | ASTM D 256 |
| Gardner, 23°C | 23 | J | ASTM D 3029 |
| Energi Total Dampak Instrumen, 23°C | 28 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 4 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 4 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 5 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 219 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 198 | °C | ASTM D 648 |
| CTE, -40°C sampai 40°C, aliran | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.5E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.5E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 200 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 205 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.36 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 16 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.2 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.65 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 21 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| UL diakui, 94V-2 Flame Class Rating (3) | 0.71 | mm | UL 94 |
| UL diakui, 94V-0 Flame Class Rating (3) | 0.71 | mm | UL 94 |
| UL diakui, 94-5VA rating (3) | 2.99 | mm | UL 94 |
| Sumber GMD, terakhir diperbarui:05/04/2007 | |||
| Pencetakan Injeksi | Nilai | Satuan | |
| Suhu Pengeringan | 150 | °C | |
| Waktu Pengeringan | 4 - 6 | jam | |
| Waktu pengeringan (kumulatif) | 24 | jam | |
| Kandungan Kelembaban Maksimal | 0.02 | % | |
| Suhu Peleburan | 350 - 400 | °C | |
| Suhu Nozzle | 345 - 400 | °C | |
| Suhu depan - Zona 3 | 345 - 400 | °C | |
| Tengah - Zona 2 Suhu | 340 - 400 | °C | |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C | |
| Suhu Cetakan | 135 - 165 | °C | |
| Tekanan Belakang | 0.3 - 0.7 | MPa | |
| Kecepatan sekrup | 40 - 70 | rpm | |
| Menembak untuk ukuran silinder | 40 - 60 | % | |
| Kedalaman ventilasi | 0.025 - 0.076 | mm | |
| Sumber GMD, terakhir diperbarui:05/04/2007 | |||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem HU1110.pdf |
|