SabikUltem HU1004resin adalahHigh Temperature, Transparan, Polyetherimide Blend dengan Duktility Ditingkatkan dan Ditingkatkan Hydrostability. Untuk perangkat medis dan aplikasi farmasi.biocompatible (ISO 10993 atau USP Kelas VI), sesuai dengan kontak makanan. EtO dan uap sterilisasi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 95 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 90 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 85 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 2900 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 140 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3000 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 50 mm/menit | 97 | MPa | ISO 527 |
| Tekanan tarik, pecah, 50 mm/menit | 80 | MPa | ISO 527 |
| Tekanan tarik, hasil, 50 mm/menit | 7 | % | ISO 527 |
| Tekanan tarik, putus, 50 mm/menit | 80 | % | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 136 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 2800 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, bertanduk, 23°C | 70 | J/m | ASTM D 256 |
| Izod Impact, Reverse Notched, 3,2 mm | 3300 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 93 | J | ASTM D 3763 |
| Total Energi Dampak Instrumen, 0°C | 99 | J | ASTM D 3763 |
| Energi Total Dampak Instrumen, -20°C | 93 | J | ASTM D 3763 |
| Duktilitas Dampak Instrumen, 23°C | 100 | % | ASTM D 3763 |
| Duktilitas Dampak Instrumen, 0°C | 100 | % | ASTM D 3763 |
| Duktilitas Dampak Instrumen, -20°C | 90 | % | ASTM D 3763 |
| Izod Impact, tidak diukir 80*10*4 +23°C | NB | kJ/m2 | ISO 180/1U |
| Izod Dampak, tidak diukir 80*10*4 -30°C | NB | kJ/m2 | ISO 180/1U |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy Impact, bertanduk, 23°C | 11 | kJ/m2 | ISO 179/2C |
| Termal | Nilai | Satuan | Standar |
| HDT, 0,45 MPa, 6,4 mm, tidak diiris | 214 | °C | ASTM D 648 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 204 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 5.6E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, xflow | 5.5E-05 | 1/°C | ASTM E 831 |
| Konduktivitas Termal | 0.19 | W/m-°C | ASTM C 177 |
| CTE, 23°C sampai 150°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C sampai 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat A/50 | 219 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0,45MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Be |
| HDT/Ae, 1,8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.28 | - | ASTM D 792 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 10 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.28 | g/cm3 | ISO 1183 |
| Tingkat Volume Peleburan, MVR pada 360°C/5,0 kg | 14 | cm3/10 menit | ISO 1133 |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 46 | % | ASTM D 2863 |
| Densitas Asap, Api, Ds 4 min | 0.7 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:10/20/2008 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 6 - 8 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 355 - 390 | °C |
| Suhu Nozzle | 345 - 390 | °C |
| Suhu depan - Zona 3 | 345 - 390 | °C |
| Tengah - Zona 2 Suhu | 335 - 390 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 390 | °C |
| Suhu Cetakan | 130 - 160 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:10/20/2008 | ||
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
 |
S-Plastics Ultem HU1004.pdf |
|