SabikUltem HU1000resin adalahTransparan, aliran standar Polyetherimide (Tg 217C). ECO Conform. Untuk perangkat medis dan aplikasi farmasi. Manajemen perubahan perawatan kesehatan, biokompatibel (ISO 10993 atau Kelas VI USP),Cocok untuk kontak makanan. EtO dan uap sterilisasi.
| Mekanis | Nilai | Satuan | Standar |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 110 | MPa | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 90 | MPa | ASTM D 638 |
| Tekanan tarik, yld, tipe I, 5 mm/menit | 7 | % | ASTM D 638 |
| Tekanan tarik, brk, tipe I, 5 mm/menit | 60 | % | ASTM D 638 |
| Tensile Modulus, 5 mm/min | 3580 | MPa | ASTM D 638 |
| Tekanan lentur, yld, 1,3 mm/menit, rentang 50 mm | 173 | MPa | ASTM D 790 |
| Flexural Modulus, 1,3 mm/menit, rentang 50 mm | 3430 | MPa | ASTM D 790 |
| Tekanan tarik, hasil, 5 mm/menit | 105 | MPa | ISO 527 |
| Tekanan tarik, pecah, 5 mm/menit | 85 | MPa | ISO 527 |
| Tekanan tarik, hasil, 5 mm/menit | 6 | % | ISO 527 |
| Tekanan tarik, istirahat, 5 mm/menit | 60 | % | ISO 527 |
| Modulus tarik, 1 mm/menit | 3200 | MPa | ISO 527 |
| Tekanan lentur, hasil, 2 mm/menit | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/menit | 3300 | MPa | ISO 178 |
| Dampak | Nilai | Satuan | Standar |
| Izod Dampak, tidak diukir, 23°C | 1335 | J/m | ASTM D 4812 |
| Izod Dampak, bertanduk, 23°C | 53 | J/m | ASTM D 256 |
| Izod Dampak, bertanduk, -30°C | 55 | J/m | ASTM D 256 |
| Energi Total Dampak Instrumen, 23°C | 0 | J | ASTM D 3763 |
| Izod Impact, bernotas 80*10*4 +23°C | 6 | kJ/m2 | ISO 180/1A |
| Izod Impact, bertanda 80*10*4 -30°C | 6 | kJ/m2 | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 4 | kJ/m2 | ISO 179/1eA |
| Termal | Nilai | Satuan | Standar |
| Vicat Softening Temperature, Tingkat B/50 | 218 | °C | ASTM D 1525 |
| HDT, 1,82 MPa, 6,4 mm, tidak diiris | 201 | °C | ASTM D 648 |
| CTE, -20°C sampai 150°C, aliran | 5.58E-05 | 1/°C | ASTM E 831 |
| CTE, -20°C sampai 150°C, xflow | 5.4E-05 | 1/°C | ASTM E 831 |
| CTE, -40°C sampai 40°C, aliran | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C sampai 40°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature, Tingkat B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temperature, Tingkat B/120 | 211 | °C | ISO 306 |
| HDT/Af, 1,8 MPa Flatw 80*10*4 sp=64mm | 215 | °C | ISO 75/Af |
| FISIK | Nilai | Satuan | Standar |
| Gravitasi Spesifik | 1.27 | - | ASTM D 792 |
| Penyerapan air, 24 jam | 0.25 | % | ASTM D 570 |
| Penyerapan air, keseimbangan, 23C | 1.25 | % | ASTM D 570 |
| Penyusutan jamur, aliran, 3,2 mm | 0.5 - 0.7 | % | Metode S-Plastics |
| Tingkat Aliran Peleburan, 337°C/6,6 kgf | 9 | g/10 menit | ASTM D 1238 |
| Kepadatan | 1.27 | g/cm3 | ISO 1183 |
| Absorpsi air, (23°C/sat) | 1.25 | % | ISO 62 |
| Penyerapan Kelembaban (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Tingkat Volume Peleburan, MVR pada 220°C/5,0 kg | 13 | cm3/10 menit | ISO 1133 |
| Listrik | Nilai | Satuan | Standar |
| Resistivitas Volume | 1.E+17 | Ohm-cm | ASTM D 257 |
| Kekuatan dielektrik, di udara, 1,6 mm | 32.7 | kV/mm | ASTM D 149 |
| Kekuatan dielektrik, dalam minyak, 1,6 mm | 27.9 | kV/mm | ASTM D 149 |
| Permittivitas relatif, 1 kHz | 3.15 | - | ASTM D 150 |
| Faktor Dissipasi, 1 kHz | 0.0013 | - | ASTM D 150 |
| Faktor Dissipasi, 2450 MHz | 0.0025 | - | ASTM D 150 |
| Resistensi busur, Tungsten {PLC} | 5 | Kode PLC | ASTM D 495 |
| Pemicu Hot Wire {PLC) | 1 | Kode PLC | UL 746A |
| Tingkat Jalur Arc Tegangan Tinggi {PLC} | 2 | Kode PLC | UL 746A |
| High Ampere Arc Ign, permukaan {PLC} | 3 | Kode PLC | UL 746A |
| Indeks Pelacakan Perbandingan (UL) {PLC} | 4 | Kode PLC | UL 746A |
| Karakteristik Api | Nilai | Satuan | Standar |
| Indeks Oksigen (LOI) | 47 | % | ASTM D 2863 |
| Densitas Asap, Api, Ds 4 min | 0.7 | - | ASTM E 662 |
| Sumber GMD, terakhir diperbarui:05/10/2007 | |||
| Pencetakan Injeksi | Nilai | Satuan |
| Suhu Pengeringan | 150 | °C |
| Waktu Pengeringan | 4 - 6 | jam |
| Waktu pengeringan (kumulatif) | 24 | jam |
| Kandungan Kelembaban Maksimal | 0.02 | % |
| Suhu Peleburan | 350 - 400 | °C |
| Suhu Nozzle | 345 - 400 | °C |
| Suhu depan - Zona 3 | 345 - 400 | °C |
| Tengah - Zona 2 Suhu | 340 - 400 | °C |
| Bagian belakang - Zona 1 Suhu | 330 - 400 | °C |
| Suhu Cetakan | 135 - 165 | °C |
| Tekanan Belakang | 0.3 - 0.7 | MPa |
| Kecepatan sekrup | 40 - 70 | rpm |
| Menembak untuk ukuran silinder | 40 - 60 | % |
| Kedalaman ventilasi | 0.025 - 0.076 | mm |
| Sumber GMD, terakhir diperbarui:05/10/2007 | ||
Tersedia di stok dengan harga yang menguntungkan
1.1000 seri
1000, MI9.0; 1010, MI18.0; Hu1000, kelas medis.
2Seri 2000, tambahkan GF
2100, tambahkan 10% GF, MI 7.0;
2110, tambahkan 10% GF, MI 11.0;
2200, tambahkan 20% GF, MI 6.0;
2210, tambahkan 20% GF, MI 8.4;
2300, tambahkan 30% GF, MI 5.0;
2310, tambahkan 30% GF, MI 7.6;
3. lainnya
MD130, MD131, AUT195, ATX200, dll.
Dalam beberapa tahun terakhir, kami telah mengembangkan pasar domestik dan secara aktif mengeksplorasi pasar luar negeri.Hingga saat ini, kami telah menyediakan produk dan layanan berkualitas tinggi untuk lebih dari 1.000 pelanggan di berbagai industri, termasuk: elektronik dan peralatan listrik, medis, makanan,elektronik otomotif, komunikasi optoelektronik, energi fotovoltaik baru, pengolahan air, transportasi dan industri lainnya.
Samtion Chemical memasok plastik teknik dan bahan khusus yang dimodifikasi dari S-Plastics dan merek lain. Produk asli kami dijamin,dengan kualifikasi lengkap dan kapasitas pasokan yang unggul dan keuntungan harga.
Setiap batch produk kami adalah subjek inspeksi kualitas yang ketat untuk memastikan pasokan asli. Semua produk memiliki sertifikat MSDS, ROHS, SGS, REACH, FDA, EU, UL, COC / COA!!
Dengan jaringan penjualan yang kuat dan kekuatan, kami memiliki layanan gudang di Guangzhou, Dongguan, zona perdagangan bebas Shenzhen,Hong Kong dan empat tempat lainnya ( persediaan produk konvensional melebihi 1000 ton). Kami dapat memberikan pelanggan dengan respon cepat, layanan profesional dan produk yang sangat baik!
|
Untuk informasi lebih lanjut silahkan unduh lembar data |
|
|
S-Plastics Ultem HU1000.pdf |
|
Dapatkan Kutipan Terbaru
Sumber distribusi tingkat pertama di Cina Selatan Mengurangi biaya pengadaan, meningkatkan stabilitas pasokan, Membantu Anda menemukan bahan plastik rekayasa yang paling cocok
|